Method of fabrication of semiconductor structures by ion implantation

ABSTRACT

The present invention relates to the formation of trench isolation structures that isolate active areas and a preferred doping in the fabrication of a CMOS device with a minimized number of masks. Ions of a P-type dopant are implanted into a semiconductor substrate having therein a P-well and an N-well. Each of the N-well and P-well has therein a trench. The ions of the P-type dopant are implanted beneath each of the trenches in the P-well and the N-well to create a first P-type dopant concentration profile in the semiconductor substrate, wherein the P-well and the N-well are substantially unimplanted by the ions of the P-type dopant in active areas adjacent to the respective trenches therein. A second implanting ions of a P-type dopant is made into the semiconductor substrate. The second implanting is beneath each of the trenches in the P-well and the N-well to form a second P-type dopant concentration profile. The second implanting is also though one or more barrier layers on the semiconductor substrate into the P-well and the N-well in active areas adjacent to each of the trenches in the P-well and the N-well to form a third P-type dopant concentration profile, wherein the second and third P-type dopant concentration profiles are simultaneously formed. Next, the respective trenches in each of the P-well and N-well are substantially filled with a dielectric material. Ions of an N-type dopant are then implanted into the N-well, wherein the P-well is substantially unimplanted by the ions of the N-type dopant, and wherein the N-well has therein a concentration of the N-type dopant that is substantially greater than the P-type dopant therein. The N-type dopant dopes active areas in the N-well so as to achieve a desired threshold voltage.

RELATED APPLICATIONS

[0001] This application is a continuation of U.S. patent application Ser. No. 09/370,497, filed on Aug. 9, 1999, which is a continuation of U.S. patent application Ser. No. 08/897,364, filed on Jul. 22, 1997, now U.S. Pat. No. 5,937,287, which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

[0002] 1. The Field of the Invention

[0003] The present invention relates to fabrication of semiconductor structures. More particularly, the present invention relates to formation of semiconductor structures by ion implantation techniques. In particular, the inventive method disclosed herein is applied to formation of a complementary metal oxide semiconductor structure that includes formation of ion-implant enhanced isolation trenches for electrical isolation of active areas. The invention is applicable to formation of semiconductor structures that require two dopants that are different or opposite in conductivity enhancement of semiconductor silicon.

[0004] 2. The Relevant Technology

[0005] In the microelectronics industry, a substrate refers to one or more semiconductor layers or structures which includes active or operable portions of semiconductor devices. In the context of this document, the term “semiconductive substrate” is defined to mean any construction comprising semiconductive material, including but not limited to bulk semiconductive material such as a semiconductive wafer, either alone or in assemblies comprising other materials thereon, and semiconductive material layers, either alone or in assemblies comprising other materials. The term substrate refers to any supporting structure including but not limited to the semiconductive substrates described above.

[0006] In the microelectronics industry, the process of miniaturization entails shrinking the size of individual semiconductor devices and crowding more semiconductor devices into a given unit area than has been previously achieved. With miniaturization, problems of device crowding arise. For example, problems of proper isolation between components arise. When miniaturization demands the shrinking of individual devices, isolation structures must also be reduced in size.

[0007] To form an isolation trench, a photoresist material is applied to a semiconductive material into which the isolation trench is to be formed, preferably by etching the semiconductive material. A beam of light, such as ultraviolet (UV) light, transfers a pattern through an imaging lens from a photolithographic template to the photoresist material. The pattern of the photolithographic template includes opaque and transparent regions with selected shapes that match corresponding openings and intact portions intended to be formed in the photoresist material. The photolithographic template is conventionally designed by computer-assisted drafting and is of a much larger size than the semiconductor structure on which the photoresist material is located. Light is directed through the photolithographic template and is focused on the photoresist coating in a manner that reduces the pattern of the photolithographic template to the size of the photolithographic coating and that develops the portions of the photoresist coating that are unmasked and are intended to remain. The undeveloped portions are thereafter easily removed. Other photolithographic techniques for formation of semiconductor structures are also possible. After the removal of the undeveloped portions of the photoresist material, the isolation trench is etched into the semiconductive material.

[0008] Isolation trenches and active areas are often doped, either to enhance conductivity around an isolation area, to increase the breakdown voltage (BV) of an active area diode which is adjacent to a field isolation trench, and/or to achieve a higher threshold voltage (V_(T)) of a parasitic field transistor.

[0009] For the fabrication of a complimentary metal oxide semiconductor (CMOS) device, ion implantation is used to form a preferred BV of an active area diode and a preferred V_(T) a parasitic field transistor. The BV and V_(T) are achieved by patterning a first mask on an N-well side of the CMOS device being fabricated. Next, dopant ions are implanted into the P-well portion of the device. Following dopant ion implantation of the P-well, the mask must be removed and the CMOS device must be patterned with a second mask on the P-well side of the CMOS device being fabricated. After patterning of the second mask, the N-well is implanted with dopant ions. This first and second mask technique is required to prevent the wrong type of dopant in each of the N-well and P-well of the CMOS device being fabricated.

[0010] The first and second mask process involves several steps which increase the possibility for fabrication errors entering into the process flow that will lower overall production yield. For example, where an isolation trench was formed by an anisotropic etch, a portion of the first mask is polymerized to begin to line the recess formed by the anisotropic etch. In such a case, stripping of the first photoresist may require a stronger stripping solution than would otherwise be needed. During photoresist polymerization, the polymerized photoresist may combine with other exposed portions of the semiconductor structure, such as contaminants, and thereby form a polymer composite film within the recess being formed. Such a polymer composite film resists stripping with conventional stripping solutions. A more effective stripping solution, however, that removes a polymer composite film will likely also cause undesirable topographies of the semiconductor structure that may compromise the integrity thereof.

[0011] What is needed is a method of ion implantation in a CMOS semiconductor structure being fabricated that achieves complimentary ion implantation with minimized masking steps in order to improve overall production yield. What is also needed is a method of CMOS fabrication that reduces destructive doping in N-well and P-well portions of a CMOS structure being fabricated while minimizing the number of masking steps.

SUMMARY OF THE INVENTION

[0012] The present invention relates to doping of a semiconductor structure using a minimal number of masks. By way of illustration, the present invention relates to the formation of trench isolation structures that isolate active areas, and relates to preferred doping in the fabrication of a CMOS device with use of a minimal number of masks. Other uses for the inventive method may include CMOS formation with field oxide regions used to separate active areas. The inventive method can be used in the fabrication or CMOS device including such structures as dynamic random-access memory (DRAM) structures, word line-activated transistors, and bipolar transistors.

[0013] In the inventive method, an isolation trench is formed in each of a P-well and an N-well, where the P-well and the N-well are situated in a semiconductor material. Each isolation trench extends below a top surface of the semiconductor material upon which is situated a pad oxide, a nitride layer, and a photoresist layer having a pattern therein through which an etchant anisotropically etched the semiconductor material so as to form the isolation trenches in each of the P-well and the N-well.

[0014] A first doping scheme is a doping of the semiconductor material with a P-type dopant, such as boron. The P-well and the N-well are both doped by ion implantation with the P-type dopant, which may include multiple doping steps. In the first doping scheme, the ions are implanted through the pad oxide, the nitride layer, and the photoresist layer into the semiconductor material. Ions that are implanted into the isolation trenches in each of the P-well and the N-well will implant deeper into the semiconductor material than ions that are implanted through the pad oxide, the nitride layer, and a photoresist layer.

[0015] The first doping scheme will preferably be two ion implantations that produce a first and a second P-type dopant concentration profile. The second P-type dopant concentration profile dopes active areas in each of the P-well and the N-well. Also, the second P-type dopant concentration profile has a beginning and ending that is deeper within the semiconductor material at comparable portions of the semiconductor material than that of the first P-type dopant concentration profile. As such, the first and second P-type dopant concentration profiles appears at differing levels at comparable portions of the semiconductor material due to the lesser energy of the first ion implantation compared to that of the second ion implantation. As such, the relative energy levels dictate the ability of the second ion implantation and the disability of the first ion implantation to penetrate through the pad oxide, the nitride layer, and the photoresist layer into the semiconductor material. The order of the first and second ion implantations can be reversed.

[0016] Following the second ion implantation, a thermal process is carried out to migrate implanted dopants into the semiconductor material, the effect of which is to flatten the first and second P-type dopant concentration profiles. A thermal oxide layer is grown in the isolation trenches of the P-well and N-well during the thermal process, and each isolation trench is filled with a dielectric material. A planarizing step then reduces the height of the structure. Next, the photoresist layer and the nitride layer are removed, leaving the dielectric material extending from each isolation trench above the pad oxide layer.

[0017] A second mask is formed over the P-well, leaving exposed the N-well of the CMOS device being fabricated. The second mask has a thickness that is selected to substantially resist ion penetration therethrough into the P-well. Next, a second doping scheme is carried out as a doping of the N-well with an N-type dopant, such as phosphorous. The second doping scheme dopes active areas adjacent to trenches in the N-well. A multiple number or ion implantations of variable energy are carried out in the doping of the N-well. As the N-well was doped with P-type dopants in the first doping scheme, the second doping scheme is sufficient to overcome the P-type dopant effect with N-type dopants. The first and second doping schemes will preferably assist in electrical isolation of active areas in each of the P-well and N-well so as to reduce leakage currents.

[0018] Energy of the implantations of the first and second doping schemes can be controlled to achieve a preferred voltage threshold (V_(T)) for a parasitic field transistor through selected dopant concentration profiles. For example, selected energies of the ion implantations can be designed to achieve a preferred trench wall and trench well implant concentration profiles, as well as a preferred deep junction implant concentration profile. Following preferred implantations, the second mask is removed as is the pad oxide layer, and a gate oxide layer in place thereof. A process flow is then conducted so that the desired CMOS structure is completed.

[0019] These and other features of the present invention will become more fully apparent from the following description and appended claims, or may be learned by the practice of the invention as set forth hereinafter.

BRIEF DESCRIPTION OF THE DRAWINGS

[0020] In order that the manner in which the above-recited and other advantages of the invention are obtained, a more particular description of the invention briefly described above will be rendered by reference to specific embodiments thereof which are illustrated in the appended drawings. Understanding that these drawings depict only typical embodiments of the invention and are not therefore to be considered to be limiting of its scope, the invention will be described and explained with additional specificity and detail through the use of the accompanying drawings in which:

[0021]FIG. 1 is an elevational cross-section view of a semiconductor substrate having a P-well and an N-well therein each of which have an isolation trench therein, where P-type ion dopants are implanted in a first of two implanted in a first doping scheme though each of the isolation trenches into the respective P-well and N-well but not through layers situated upon the semiconductor substrate which include a pad oxide, a nitride layer and a photoresist patterned layer, and where a first P-type dopant concentration profile is illustrated at the bottom of the isolation trench in each of the P-well and the N-well, and furthermore illustrating a graph of dopant concentration as a function of depth in the semiconductor substrate for the P-type dopant concentration profiles at the bottom of the isolation trench in each of the P-well and the N-well.

[0022]FIG. 2 is an elevational cross-section view of the semiconductor structure depicted in FIG. 1, wherein a second P-type ion implantation has been carried out for the first doping scheme, where the second P-type ion implantation penetrates the pad oxide, the nitride layer and the photoresist patterned layer so as to implant P-type dopant into both the P-well and the N-well so to form a second P-type dopant concentration profile below the first doping concentration profile at comparable locations below the isolation trenches, and also being formed beneath the pad oxide within both the P-well and the N-well.

[0023]FIG. 3 is an elevational cross-section view of the semiconductor structure depicted in FIG. 2 after further processing, wherein the photoresist patterned layer has been stripped and a thermal process has caused an oxide and an optional oxynitride layer to form within the isolation trenches and upon the nitride layer, respectively, where the first and second P-type doping concentration profiles have flattened due to dopant migration during such thermal processing, where a dielectric material is illustrated as having been formed over the oxide and optional oxynitride layer to substantially fill the isolation trenches within both the P-well and the N-well, and wherein a level is indicated in phantom above which all material will be removed in a planarizing step.

[0024]FIG. 4 is an elevational cross-section view of the semiconductor structure depicted in FIG. 3 after further processing, where the oxide, the optional oxynitride layer, and the nitride layer have been removed, where the P-well has been substantially covered with a mask to prevent ion implantation therein, wherein the N-well is exposed by the same mask, and wherein N-type ion dopants have been implanted into the N-well in a second doping scheme involving multiple ion implantation of varied energies so as to achieve within the N-well a doped active area, a doped trench wall and well, and a doped deep junction.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0025] The present invention relates to doping of a semiconductor structure using a minimal number of masks, and relates to the formation of an isolation trench that electrically isolates active areas in the fabrication of a CMOS device with a minimal number of masking steps. Other uses for the inventive method may include formation of field oxide regions that electrically isolate active areas. The inventive method can be used in the fabrication of CMOS devices including dynamic random-access memory (DRAM), word line-activated transistors, and bipolar transistors.

[0026]FIG. 1 illustrates an elevational cross-section view of a semiconductor structure 10 that includes a semiconductor substrate 12 that is composed, for example, of single crystal silicon. Semiconductor substrate 12 is illustrated as having two sections divided into a P-well 15 and an N-well 17. Each of P-well 15 and N-well 17 has an active area 14 electrically isolated, respectively, by an isolation trench 22, 24. Upon active area 14 is a pad oxide layer 16 that has a nitride layer 18 disposed thereupon. Upon nitride layer 18, a mask 20 is patterned to exposed isolation trenches 22, 24. An etchant passes through openings in mask 20 to anisotropic etch isolation trenches 22, 24 in semiconductor substrate 12.

[0027] In a first doping step of a first doping scheme, downwardly-directed arrows represent P-type ions, such as boron, that are implanted beneath exposed isolation trenches 22, 24 in semiconductor substrate 12, but not through pad oxide layer 16 or nitride layer 18. As a result, a first P-type dopant concentration profile 26 has been formed. First P-type dopant concentration profile 26 is illustrated in FIG. 1 as a curve to reflect, both positionally within semiconductor substrate 12 and graphically, the non-linear or varying concentration of P-type dopant concentration as a function of depth within semiconductor substrate 12. Similarly, in FIGS. 2-4, dopant concentration profiles therein also reflect positional and quantitative representations of the implanted dopant.

[0028]FIG. 2 illustrates further processing according to the inventive method applied to the structure seen in FIG. 1, where mask 20 has been stripped, and a second P-type ion implantation of the first implant scheme has been made into both the P-well and the N-well. the energy of the second P-type ion implantation is sufficient to penetrate through pad oxide 16 and silicon nitride layer 18 into semiconductor substrate 12 and thereby form a second P-type dopant concentration profile 28. Second P-type dopant concentration profile 28 in P-well 15 functions as a P-well implant or an soft error rate barrier. Second P-type dopant concentration profile 28 appears substantially beneath first P-doping concentration profile 26 at the bottom of both isolation trenches 22, 24. As the first P-type ion implantation did not have sufficient energy to penetrate through pad oxide 16 and silicon nitride layer 18 into semiconductor substrate 12, only second P-type dopant concentration profile 28 appears within active area 14. There are two locations in semiconductor substrate that second P-doping concentration profile 28 appear, which are immediately below pad oxide layer 16 at a lesser depth than a second location beneath isolation trenches 22, 24. The two locations for second P-type dopant concentration profile 28 are due to the penetration of ions implanted in the first location through both nitride layer 18 and pad oxide layer 16 and the absence of such penetration by ions implanted in the second location. Additionally, the ions implanted in the second location began penetration into semiconductor substrate 12 deeper than the ions implanted in the first location due to the presence of isolation trenches 22, 24.

[0029]FIG. 3 reflects the result of the structure seen in FIG. 2 being subject to a thermal process. It can be seen that first and second P-type dopant concentration profiles 26, 28 are substantially flattened compared with those depicted in FIGS. 1 and 2. This flattening of dopant concentration profiles illustrates the effect of dopant migration from the thermal process. It can be seen that first P-type dopant concentration profile 26 has formed a thermally adjusted first P-type dopant concentration profile 30, and second P-type dopant concentration profile 28 has formed a thermally adjusted second P-type dopant concentration profile 32.

[0030] A thermal oxide layer 34 has also formed within both P-well 22 and N-well 24. An optional thermal oxynitride layer 36 may also form upon nitride layer 18. The optional formation of optional thermal oxynitride layer 36 will depend upon the atmosphere, temperature, and duration of thermal processing conditions.

[0031] Following thermal processing, a dielectric material, for example silicon dioxide, is used to fill isolation trenches 22, 24 so as to form filled trenches 38. Silicon dioxide can be conventionally formed, such as by chemical vapor deposition using a tetraethylorthosilicate precursor. It can be seen that a filled trench 38 is formed, respectively, in isolation trench 22 in P-well 15, and insolation trench 17 in N-well trench 17. Next, a height reduction step, preferably a planarizing step such as chemical mechanical planarization is conducted at section line A-A seen in FIG. 3 so as to remove substantially all material extending above section line A-A. Another step is then conducted in which nitride layer 18 is removed from the surface of pad oxide 16. Nitride layer 18 and optional thermal oxynitride layer 36 are removed preferably by a phosphoric acid wet etch that has an etch recipe selective to oxides of silicon such as pad oxide 16 and filled trench 38. What remains of filled trench 38, thermal oxide layer 34, and optional thermal oxynitride layer 36 is isolation structure 40 seen in FIG. 4 which extends, respectively, from isolation trenches 22, 24 above an upper surface 52 of pad oxide 16. The distance that isolation structure 40 extends above upper surface 52 is dictated by the thickness of nitride layer 18 and the degree of selectivity of the nitride etch to the dielectric that forms filled trench 38 over nitride layer 18.

[0032] As seen in FIG. 4, a second mask 50 has been formed over the P-well 15, leaving N-well 17 exposed. Second mask 50 is selected from a thickness range that will substantially resist ions from penetrating therethrough. Preferably, second mask 50 has a thickness in a range from about 2 microns to about 6 microns, more preferably about 2.5 microns to about 5.5 microns, and most preferably about 3 microns to about 5 microns.

[0033] Second mask in then patterned as desired, such as by photolithography. Following patterning of second mask 50, a second doping scheme is undertaken. The second doping scheme involves N-type ion implantation, such as phosphorous ions, in multiple implantations of varying energy. Mask 50 prevents doping P-well 15 with N-type dopant, whereas N-well 17 is doped by the N-type ions implanted therein. The second doping scheme includes up to four N-type ion implantations in order to impart preferred properties.

[0034] In FIG. 4, it can be seen that four implants have been carried out in the second doping scheme. In the second doping scheme, P-well 15 of semiconductor substrate 12 has been substantially shielded from implantation due to the presence of second mask 50. As such, the P-type doping of P-well 15 of semiconductor substrate 12 is substantially unchanged following the second doping scheme. It is preferred that the second doping scheme prevent N-type dopants from penetrating through second mask 50 in a range from about 90 to 100 percent, more preferably from greater than 95 percent to about 100 percent, more preferably from greater than 99 percent to about 100 percent, and most preferably greater than 99.9 percent.

[0035] For N-well 17 of semiconductor substrate 12, several implantations each varying in energy may be carried out to achieve each of a preferred V_(T) implant concentration profile 42, a preferred trench wall implant concentration profile 44, a preferred compensating trench well implant concentration profile 46, and a preferred compensating deep junction implant concentration profile 48 for the N region of semiconductor structure 10. Implant concentration profiles 42-48 are illustrated without being superimposed upon implant concentration profiles 30-32 for the sake of clarity. It is understood, however, that implant concentration profiles 42-48 are intermingled with implant concentration profiles 30-32 in N-well 17 of semiconductor substrate 12. Isolation structure 40 in N-well 17 is doped with N-type dopant from the second doping scheme, as seen by implant concentration profiles 42 and 44 therein. Doping within isolation structure 40 in N-well 17 will not significantly alter the dielectric properties thereof An etchant, however, may have a changed selectivity to the silicon dioxide within isolation structure 40 within N-well 17 have N-type doping due. Following preferred implantations, second mask 50 is stripped and pad oxide layer 16 is optionally removed in order to grow a gate oxide layer (not shown) in its place. Further process flow steps can then be performed to complete a CMOS device.

[0036] The effect of ion implantation will preferably strike a balance between overcoming P-type doping in N-well 17, and in forming a preferred N-type doping in N-well 17. N-type doping concentrations may exceed P-type doping concentrations in N-well 17 by as much as 100 times in order to overcome P-type doping therein as preferred.

[0037] To further illustrate an example of a preferred second doping scheme, it is known that the voltage threshold (V_(T)) for parasitic field transistors in N-well and P-well in a CMOS device, such as active areas 14, are preferred to have substantially comparable magnitudes for optimal logic-gate performance. In the present invention, the second doping scheme for N-well 17 requires a doping concentration that first neutralizes the effect of the P-type doping of the first P-doping scheme, and that then achieves a desired V_(T) for parasitic field transistors in N-well 17 to about the same V_(T) for parasitic field transistors in P-well 15.

[0038] The inventive method assists in the isolation of active areas by a preferred dopant concentration of implanted ions under the active areas being isolated. Also, the implantation techniques of the inventive method will preferably reduce leakage currents between the P-well and N-well. By implanting the P-well under both the active area and the isolation trench according to the inventive method, the soft error rate of a CMOS device, such as a memory cell, can be reduced. Additionally, the breakdown voltage for an active area diode and for an N-well diode is increased by ion implantation according to the inventive method.

[0039] The present invention may be embodied in other specific forms without departing from its spirit or essential characteristics. The described embodiments are to be considered in all respects only as illustrated and not restrictive. The scope of the invention is, therefore, indicated by the appended claims and their combination in whole or in part rather than by the foregoing description. All changes that come within the meaning and range of equivalency of the claims are to be embraced within their scope. 

What is claimed and desired to be secured by United States Letters Patent is:
 1. A method of doping a semiconductor device that includes a plurality of layers on a semiconductor substrate, comprising: directing ions of a first type toward said semiconductor device through a trench extending into said semiconductor device and terminating within the semiconductor substrate; directing ions of a second type toward said semiconductor device; and protecting a portion of said semiconductor device from said ions of said second type; wherein: said semiconductor device includes a nitride layer that is over an oxide layer, the oxide layer being over a semiconductor substrate having an active area, the structure also including the trench, said trench extending through the nitride layer and the oxide layer, and terminating within the semiconductor substrate beneath the active area; and directing ions of a second type toward said semiconductor device further comprises: removing the nitride layer over the oxide layer; implanting said ions of said second type into the semiconductor substrate, said ions of said second type passing: through the oxide layer and through dielectric material previously formed in the trench.
 2. The method as defined in claim 1, wherein the ions of said second type provide a conductivity that is opposite to that provided by the ions of the first type.
 3. The method as defined in claim 1, wherein the ions of said first type comprise boron ions and the ions of said second type comprise phosphorous ions.
 4. The method as defined in claim 1, wherein said directing ions of a first type towards said semiconductor device implants ions of said first type into the semiconductor substrate, and ions of said second type are implanted into the semiconductor substrate to a depth that is greater than the depth to which the ions of said first type are implanted.
 5. A method of doping a semiconductor device that includes a plurality of layers on a semiconductor substrate, comprising: directing ions of a first type toward said semiconductor device through a trench extending into said semiconductor device and terminating within the semiconductor substrate; directing ions of a second type toward said semiconductor device; and protecting a portion of said semiconductor device from said ions of said second type, wherein: said semiconductor device includes a mask layer over a nitride layer that is over an oxide layer, the oxide layer being over a semiconductor substrate having an active area therein, the structure also including the trench, said trench extending through the mask layer, the nitride layer and the oxide layer, and terminating within the semiconductor substrate beneath the active area; directing ions of a first type toward said semiconductor device further comprises: implanting said ions of said first type into the active area through the trench; removing the mask layer over the nitride layer; and implanting said ions of said first type into the semiconductor substrate, said ions of said first type passing: through the trench into the semiconductor substrate; and through both the nitride layer and the oxide layer; and directing ions of a second type toward said semiconductor device further comprises: removing the nitride layer over the oxide layer; implanting said ions of said second type into the semiconductor substrate, said ions of said second type passing: through the oxide layer; and through dielectric material previously formed in the trench.
 6. The method as defined in claim 5, wherein the ions of said second type provide a conductivity that is opposite to that provided by the ions of said first type.
 7. The method as defined in claim 5, wherein the ions of said first type comprise boron ions and the ions of said second type comprise phosphorous ions.
 8. The method as defined in claim 5, wherein the ions of said first type consist essentially of boron ions and the ions of said second type consist essentially of phosphorous ions.
 9. The method as defined in claim 5, wherein ions of said second type are implanted into the semiconductor substrate to a depth that is greater than the depth to which the ions of said first type are implanted.
 10. The method as defined in claim 5, wherein said ions of said first type are implanted into a limited portion of the active area.
 11. A method of doping a CMOS device having a first active area, a second active area, and at least one protective layer over said first and second active areas, the method comprising: initiating a first implantation stage of a first type of ions onto said CMOS device through one of a first trench in the first active area and a second trench in the second active area, wherein initiating said first implantation stage of said first type of ions onto said CMOS device further comprises implanting said first type of ions over generally the entire CMOS device; removing said at least one protective layer; initiating a second implantation stage of said first type of ions onto said CMOS device; providing said first active area with an additional protective layer; and initiating a first implantation stage of a second type of ions onto said CMOS device.
 12. The method as defined in claim 11, wherein initiating said second implantation stage of said first type of ions onto said CMOS device further comprises: implanting said first type of ions over generally the entire CMOS device.
 13. The method as defined in claim 11, wherein said first type of ions and said second type of ions provide the same type of conductivity.
 14. The method as defined in claim 11, wherein the ions of said second type provide a conductivity that is opposite to that provided by the ions of said first type.
 15. The method as defined in claim 11, wherein the first type of ions comprises boron ions and the second type of ions comprises phosphorous ions.
 16. In a structure that includes a mask layer over a protective layer that is over a semiconductor substrate having an active area therein, the structure also including a trench that extends through the mask layer and the protective layer, and terminates within the semiconductor substrate beneath the active area, a doping method comprising: implanting a first dopant into the active area through the trench; removing the mask layer over the protective layer; and implanting a second dopant into the semiconductor substrate, said dopant passing: through the trench into the semiconductor substrate; and through the protective layer.
 17. The doping method as defined in claim 16, further comprising: filling the trench with a dielectric material.
 18. The method as defined in claim 17, further comprising: removing a portion of the protective layer leaving a remaining portion thereof; implanting a third dopant into the semiconductor substrate, said dopant passing: through said remaining portion of the protective layer; and through the dielectric material in the trench.
 19. The method as defined in claim 18, wherein the third dopant provides a conductivity that is opposite to that provided by the first and second dopants.
 20. The method as defined in claim 18, wherein the first and the second dopants provide the same type of conductivity. 